The optimization of parameters is crucial in the joining process, particularly in welding,
to attain connections with exceptional mechanical properties. In the present study, the
welding of aluminium 6061 was conducted with a TIG, an acronym for tungsten inert
gas, is formally referred to as gas tungsten arc welding (GTAW) technique, employing
a suitable ER 4043 electrode and argon shielding gas. The investigation of optimal
welding parameters, specifically current, voltage, and flow rate, is conducted utilizing
statistical methodologies such as the hybrid Grey-based Taguchi process. The desired
attributes for high-quality welds were established as having high tensile strength,
hardness, and a low rate of corrosion. Given the presence of three responses and one
objective, the hybrid Grey-based Taguchi method is employed. The statistical
approaches have converged on optimal parameters of 120 A, 20 V, and 15 L/min. The
present analysis reveals that the ideal welded junction exhibited the following
characteristics: a tensile strength of 190.169 MPa, a hardness value of 77HV, and a
corrosion rate of 0.29 mm. The current parameter was found to have the highest
contribution, accounting for 65.66% of the overall performance of the weldments.
Confirmatory testing was conducted in order to confirm the optimization strategy, and
the findings indicated that the Grey-based Taguchi technique is a straightforward yet
effective approach for optimizing welded connections across several performance
criteria